• fabrication and thermoelectric power factor of cosb3 prepared using modified polyol process and evacuated- and-encapsulated sintering

    جزئیات بیشتر مقاله
    • تاریخ ارائه: 1392/07/24
    • تاریخ انتشار در تی پی بین: 1392/07/24
    • تعداد بازدید: 738
    • تعداد پرسش و پاسخ ها: 0
    • شماره تماس دبیرخانه رویداد: -
      various reaction temperatures have been investigated to stabilize the cosb3 phase obtained by a modified polyol process using a refluxing condenser. the resulting powders were cold-pressed and sintered in an evacuated-and- encapsulated ampoule for transport measurements. single-phase cosb3 could be produced for the reaction carried out at 448 k for a short duration of 15 min followed by evacuated-and-encapsulated sintering at 848 k for 5 h. in comparison with the sample sintered at 798 k, the sample sintered at 848 k exhibits lower resistivity and thermopower. due to the sign crossover of the thermopower, the latter sample shows lower power factor for temperatures above 475 k.

سوال خود را در مورد این مقاله مطرح نمایید :

با انتخاب دکمه ثبت پرسش، موافقت خود را با قوانین انتشار محتوا در وبسایت تی پی بین اعلام می کنم
مقالات جدیدترین رویدادها
مقالات جدیدترین ژورنال ها