• enhanced thermoelectric properties of (pbte)0.88(pbs)0.12 composites by sb doping

    جزئیات بیشتر مقاله
    • تاریخ ارائه: 1392/07/24
    • تاریخ انتشار در تی پی بین: 1392/07/24
    • تعداد بازدید: 669
    • تعداد پرسش و پاسخ ها: 0
    • شماره تماس دبیرخانه رویداد: -
      the effects of sb doping on (pbte)0.88(pbs)0.12 composites prepared by melting, ball milling, and spark plasma sintering were investigated. the x-ray diffraction results indicate that all samples sb xpb1−x te0.88s0.12 with x = 0, 0.002, 0.004, 0.006 and 0.008 are composites containing pbte with nacl-type structure as the major phase and pbs with nacl-type structure as the minor phase. the electrical resistivity is reduced with increasing sb doping, from 1.95 × 10−5 ωm for sb content x = 0 to 5.55 × 10−6 ωm for x = 0.008 at 298 k, showing that sb is an efficient electron donor. however, the absolute seebeck coefficient decreases, from 196 μv/k for x = 0 to 57.0 μv/k for x = 0.008 at 298 k, and the thermal conductivity increases, from 0.989 w/m k for x = 0 to 1.64 w/m k forx = 0.008, with sb doping. the power factor and figure of merit zt can be enhanced by proper sb doping. the maximum dimensionless figure of merit zt of 1.20 was obtained in the sample sb0.004pb0.996te0.88s0.12 at 773 k.

سوال خود را در مورد این مقاله مطرح نمایید :

با انتخاب دکمه ثبت پرسش، موافقت خود را با قوانین انتشار محتوا در وبسایت تی پی بین اعلام می کنم
مقالات جدیدترین رویدادها
مقالات جدیدترین ژورنال ها