  • thermoelectric properties of the entire composition range in mg2si0.9925−x sn x sb0.0075

    نویسندگان :
    کلمات کلیدی :
    جزئیات بیشتر مقاله
    • تاریخ ارائه: 1392/07/24
    • تاریخ انتشار در تی پی بین: 1392/07/24
    • تعداد بازدید: 804
    • تعداد پرسش و پاسخ ها: 0
    • شماره تماس دبیرخانه رویداد: -
      eleven samples of nominal composition mg2.2si0.9925−x sn x sb0.0075 with x = 0, 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, 0.9925 were prepared by induction melting, ball milling, and spark plasma sintering. hall effect, resistivity, seebeck coefficient, and thermal conductivity measurements were conducted from room temperature to 400°c. six of the samples were investigated for thermal stability by measuring powder x-ray diffraction while heating to 400°c. all samples were stable in air during the ∼12-h-long data collection, except for mg2.2sn0.9925sb0.0075, which showed development of an elemental sn phase after heating. the lattice parameter of each sample was extracted through rietveld refinement and revealed a linear dependency on nominal composition. measurement of top and bottom of the pellets exhibited systematic differences in lattice parameter and seebeck coefficient, indicating that stoichiometry gradients are created during sintering.

سوال خود را در مورد این مقاله مطرح نمایید :

با انتخاب دکمه ثبت پرسش، موافقت خود را با قوانین انتشار محتوا در وبسایت تی پی بین اعلام می کنم
مقالات جدیدترین رویدادها
مقالات جدیدترین ژورنال ها