  • combined effects of different heat treatments and cu element on transformation behavior of niti orthodontic wires

    نویسندگان :
    کلمات کلیدی :
    جزئیات بیشتر مقاله
    • تاریخ ارائه: 1394/01/01
    • تاریخ انتشار در تی پی بین: 1394/01/01
    • تعداد بازدید: 855
    • تعداد پرسش و پاسخ ها: 0
    • شماره تماس دبیرخانه رویداد: -
     the shape memory nickel–titanium alloy has been applied in many fields due to its unique thermal and echanical performance. one of the successful applications of niti wires is in orthodontics because of its good characteristics such as low stiffness, high spring back, high stored energy, biocompatibility, superelasticity and shape memory effect. the mechanical properties of wires are paid special attention which results in achieving continuous optimal forces and eventually causing rapid tooth movement without any damage. the behavior of the alloy can be controlled by chemical composition and thermo-mechanical treatment during the manufacturing process. in this study two kinds of commercial superelastic niti archwires of 0.41 mm diameter were investigated: copper niti and highland metal. the chemical analysis of both wires was estimated by energy dispersive spectroscopy (eds). it was showed that copper niti wire contained copper and chromium. the two types of wires were exposed to different heat treatment conditions at 400 and 500 ◦c for 10 and 60 min to compare the behavior of the wires at aged and as-received conditions. phase transformation temperatures clarified by differential scanning calorimetry (dsc) showed b2 ←→ r ←→ b19 transformation in highland metal wire and b2 ←→ b19′ transformation in copper niti wire. three point bending (tpb) tests in the certain designed fixture were performed at 37 ◦c to evaluate the mechanical behavior of the wires. the experimental results revealed the superelastic behavior of the highland metal wire after 60 min ageing at 400 and 500 ◦c and the plastic deformation of the copper niti wire after annealing due to the effect of copper in the alloy composition.

سوال خود را در مورد این مقاله مطرح نمایید :

با انتخاب دکمه ثبت پرسش، موافقت خود را با قوانین انتشار محتوا در وبسایت تی پی بین اعلام می کنم
مقالات جدیدترین رویدادها
مقالات جدیدترین ژورنال ها