  • silanized tio2 nanoparticles and their application in toner as charge control agents: preparation and characterization

    نویسندگان :
    کلمات کلیدی :
    جزئیات بیشتر مقاله
    • تاریخ ارائه: 1392/01/01
    • تاریخ انتشار در تی پی بین: 1392/01/01
    • تعداد بازدید: 503
    • تعداد پرسش و پاسخ ها: 0
    • شماره تماس دبیرخانه رویداد: -
     surface modification of tio2 nanoparticles with 3-methacrylic acyloxy propyl trimethoxysilane (kh570) was carried out in the liquid phase. as additives, the modified tio2 nanoparticles were employed as charge control agents (ccas) in the toner. the hydroxyl groups on the surface of tio2 nanoparticles can interact with methoxy groups of kh570 and an organic coating layer formed. the tisingle bondosingle bondsi bond was testified by fourier transform infrared spectra (ftir). through transmission electron micrograph (tem) observation, it was found that the organic coating layer was about ∼3.1 nm and the dispersibility of the modified tio2 nanoparticles were obviously improved. static water contact angle was used to investigate the wettability of the modified tio2 surfaces. the results indicated that the hydrophobicity of the modified tio2 nanoparticle surfaces could be effectively improved as the amount of the coated kh570 increased. the specific surface area (ssa) of the modified tio2 was determined by brunauer–emmet–teller (bet) method. surface morphology of the modified toner and the toner charge were investigated by scanning electron microscopy (sem) and electrometer, respectively. the modified toner showed smoother surface and the toner charge was adjusted by the modified tio2 nanoparticles. the charge-to-mass ratio (q/m) values shifted to the negative direction, for example −13.25 μc/g, with an increasing coated kh570, probably due to the oh groups existing on the surface of tio2.

سوال خود را در مورد این مقاله مطرح نمایید :

با انتخاب دکمه ثبت پرسش، موافقت خود را با قوانین انتشار محتوا در وبسایت تی پی بین اعلام می کنم
مقالات جدیدترین رویدادها
مقالات جدیدترین ژورنال ها