• corrosion and fatigue failure analysis of a forced draft fan blade

    جزئیات بیشتر مقاله
    • تاریخ ارائه: 1390/01/01
    • تاریخ انتشار در تی پی بین: 1390/01/01
    • تعداد بازدید: 774
    • تعداد پرسش و پاسخ ها: 0
    • شماره تماس دبیرخانه رویداد: -
     the present work was carried out to investigate the failure mechanism of a power plant forced draft fan (fdf) blade made of 2014-t6 al alloy, using visual examination, microstructural characterizations, study of the fracture surface and hardness testing. based on the obtained results, surface defects including corrosion pits due to the existence of cl ion and also erosion pits due to mechanical action of particles in the air entering from the filtration system and abrading on the fan blades surfaces, increased the probability of surface crack initiation. cyclic loading and stress concentration on these surface defects influenced the fatigue life of the blade due to elevating the mean stress and resulted in fatigue failure of the investigated fdf component.

سوال خود را در مورد این مقاله مطرح نمایید :

با انتخاب دکمه ثبت پرسش، موافقت خود را با قوانین انتشار محتوا در وبسایت تی پی بین اعلام می کنم
مقالات جدیدترین رویدادها
مقالات جدیدترین ژورنال ها