  • the investigation of abnormal particle-coarsening phenomena in friction stir repair weld of 2219-t6 aluminum alloy

    نویسندگان :
    کلمات کلیدی :
    جزئیات بیشتر مقاله
    • تاریخ ارائه: 1390/01/01
    • تاریخ انتشار در تی پی بین: 1390/01/01
    • تعداد بازدید: 554
    • تعداد پرسش و پاسخ ها: 0
    • شماره تماس دبیرخانه رویداد: -
     the single-pass friction stir weld of aluminum 2219-t6 with weld-defects was repaired by overlapping friction stir welding technique. however, without any post weld heat treatment process, it was found that the phenomena of abnormal particle-coarsening of al2cu had occurred in the overlapping friction stir repair welds. the detecting results of non-destructive x-ray inspection proved that not only one group of repair fsw process parameters could lead to occurrence of the abnormal phenomena. and the abnormally coarsened particles always appeared on the advancing side of repair welds rather than the retreating side where the fracture behaviors occurred after mechanical tensile testing. the size of the biggest particle lying in the dark bands of ‘onion-rings’ was more than 150 μm. after the related investigation by scanning electron microscope and x-ray energy spectrometer, three types of formation mechanisms were proposed for reasonably explaining the abnormal phenomenon: aggregation mechanism, diffusion mechanisms i and ii. aggregation mechanism was according to the motion-laws of stir-pin. diffusion mechanisms were based on the classical theories of precipitate growth in metallic systems. the combined action of the three detailed mechanisms contributed to the abnormal coarsening behavior of al2cu particles in the friction stir repair weld.

سوال خود را در مورد این مقاله مطرح نمایید :

با انتخاب دکمه ثبت پرسش، موافقت خود را با قوانین انتشار محتوا در وبسایت تی پی بین اعلام می کنم
مقالات جدیدترین رویدادها
مقالات جدیدترین ژورنال ها