• preparation, structure and electrical conductivity of pyrochlore-type samarium–lanthanum zirconate ceramics

    کلمات کلیدی :
    جزئیات بیشتر مقاله
    • تاریخ ارائه: 1390/01/01
    • تاریخ انتشار در تی پی بین: 1390/01/01
    • تعداد بازدید: 418
    • تعداد پرسش و پاسخ ها: 0
    • شماره تماس دبیرخانه رویداد: -
     a series of zirconate compounds with the general formula sm2–xlaxzr2o7 (0 ⩽ x ⩽ 1.0) were prepared by pressureless-sintering method at 1973 k for 10 h in air. the relative density, structure and electrical conductivity of sm2–xlaxzr2o7 ceramics were investigated by the archimedes method, x-ray diffraction and impedance spectroscopy measurements. sm2–xlaxzr2o7 (0 ⩽ x ⩽ 1.0) ceramics exhibit a pyrochlore-type structure. the measured electrical conductivity of sm2–xlaxzr2o7 ceramics obeys the arrhenius relation and gradually increases with increasing temperature from 673 to 1173 k. sm2–xlaxzr2o7 ceramics are oxide-ion conductors in the oxygen partial pressure range of 1.0 × 10−4 to 1.0 atm at all test temperature levels. the electrical conductivity of sm2–xlaxzr2o7 ceramics decreases with increasing lanthanum content at identical temperature levels.

سوال خود را در مورد این مقاله مطرح نمایید :

با انتخاب دکمه ثبت پرسش، موافقت خود را با قوانین انتشار محتوا در وبسایت تی پی بین اعلام می کنم
مقالات جدیدترین رویدادها
مقالات جدیدترین ژورنال ها