  • microstructure and mechanical properties of dissimilar materials joints between t92 martensitic and s304h austenitic steels

    نویسندگان :
    کلمات کلیدی :
    جزئیات بیشتر مقاله
    • تاریخ ارائه: 1390/01/01
    • تاریخ انتشار در تی پی بین: 1390/01/01
    • تعداد بازدید: 397
    • تعداد پرسش و پاسخ ها: 0
    • شماره تماس دبیرخانه رویداد: -
     in this paper, t92 martensitic steel and s304h austenitic steel were welded by gas tungsten arc welding (gtaw) process. microstructural features and mechanical properties of t92 and s304h dissimilar materials joints were investigated. the results showed that the part of the joints with relatively weak tensile strength was t92 coarse-grained heat affected zone (cghaz), while the part of the joints which revealed relatively weak toughness was weld metal. the decrease of tensile strength in t92 cghaz was due to its coarse tempered martensite structure. weak toughness of the joints was resulted from the coarse dendritic austenite of the weld metal. however, the weld metal in transverse direction of the joints was provided higher tensile strength by the orientation distribution of grains compared with t92 cghaz.

سوال خود را در مورد این مقاله مطرح نمایید :

با انتخاب دکمه ثبت پرسش، موافقت خود را با قوانین انتشار محتوا در وبسایت تی پی بین اعلام می کنم
مقالات جدیدترین رویدادها
مقالات جدیدترین ژورنال ها