     contrast fatigue tests were carried out on t-shape tubular joints of 20 steel in three conditions: as welded, treated by ultrasonic peening treatment (upt) before loading and upt under loading. results are: (1) dispersity of test results measured by nominal stress is much larger than that measured by hot spot stress. after upt before loading, fatigue strength of 20 steel tubular joints measured by hot spot stress increases by 67% and fatigue life is prolonged by 22–45 times. (2) under low stress ratio r, upt before loading can improve the fatigue performance of welded tubular joints significantly. (3) under high stress ratio r, upt under loading (static load) is recommended to improve the fatigue performance of welded tubular joints. upt under loading not only enhances the fatigue properties at low stress level, but also at high stress level. (4) the general rule of s–ncurves of welded joints treated by upt is commonly effected by external load (static load) and self release of residual stress.

سوال خود را در مورد این مقاله مطرح نمایید :

با انتخاب دکمه ثبت پرسش، موافقت خود را با قوانین انتشار محتوا در وبسایت تی پی بین اعلام می کنم
مقالات جدیدترین رویدادها
مقالات جدیدترین ژورنال ها