    evolution of the structural and electrical properties of gete under different annealing conditions
    gete films were found to exhibit chemical, structural, and electrical changes depending on the crystal structure and annealing atmosphere. amorphous gete was converted to cubic crystalline gete after annealing treatment at 400°c. subsequent annealing in air induced phase transitions in the cubic gete, resulting in the formation of ge oxide as the major phase and metallic te as the minor phase. however, gete films deposited at 200°c maintained the rhombohedral structure regardless of the annealing time or atmosphere.

سوال خود را در مورد این مقاله مطرح نمایید :

با انتخاب دکمه ثبت پرسش، موافقت خود را با قوانین انتشار محتوا در وبسایت تی پی بین اعلام می کنم
مقالات جدیدترین رویدادها
مقالات جدیدترین ژورنال ها