• hydrothermal synthesis and characterization of novel pbwo4 microspheres with hierarchical nanostructures and enhanced photocatalytic performance in dye degradation

    جزئیات بیشتر مقاله
    • تاریخ ارائه: 1392/01/01
    • تاریخ انتشار در تی پی بین: 1392/01/01
    • تعداد بازدید: 534
    • تعداد پرسش و پاسخ ها: 0
    • شماره تماس دبیرخانه رویداد: -
     novel pbwo4 crystals with different morphologies, 14-faceted polyhedrons, hierarchical microspheres and nanoparticles, were fabricated by adjusting ph value under hydrothermal conditions. the as-prepared pbwo4 samples were characterized by nitrogen-physical adsorption, powder x-ray diffraction, scanning electron microscopy, transmission electron microscopy, uv–vis diffuse reflectance spectra, photoluminescence emission spectroscopy, and fourier transform infrared spectroscopy. the photocatalytic performance of the pbwo4 crystals with different nanostructures in degradation of the acid orange ii dye under uv light (365 nm) was investigated. the plausible growth mechanisms for pbwo4 crystals with different morphologies were proposed. photocatalytic tests showed that the performance of pbwo4 crystals strongly depended on their morphologies. pbwo4 microspheres with hierarchical nanostructures prepared under ph 7.0 at 140 °c exhibited the highest activity and stability in recycling reaction. the degradation kinetics of dye over pbwo4crystals was found to conform to the pseudo-first order model. the enhanced photocatalytic performance was attributed to the unique hierarchical nanostructures with high surface area and improved surface properties. moreover, the high crystallinity of pbwo4 microspheres exhibited an enhanced catalytic activity owing to lower recombination rate of photo-generated electron/hole pairs. these novel hierarchical pbwo4 microspheres hold promise in applications of environmental purification.

سوال خود را در مورد این مقاله مطرح نمایید :

با انتخاب دکمه ثبت پرسش، موافقت خود را با قوانین انتشار محتوا در وبسایت تی پی بین اعلام می کنم
مقالات جدیدترین ژورنال ها