  • study of microstructural evolution and mechanical properties exhibited by non alloyed ductile iron during conventional and stepped austempering heat treatment

    نویسندگان :
    کلمات کلیدی :
    جزئیات بیشتر مقاله
    • تاریخ ارائه: 1390/01/01
    • تاریخ انتشار در تی پی بین: 1390/01/01
    • تعداد بازدید: 445
    • تعداد پرسش و پاسخ ها: 0
    • شماره تماس دبیرخانه رویداد: -
     it was evaluated the microstructural and mechanical response that a non alloyed ductile iron (di) presented when was subjected to conventional austempering (ca) and stepped austempering (sa) heat treatments. x-ray diffraction (xrd) quantification techniques demonstrated to be the more reliable method for monitoring phase transformations taking place during both ca and sa. when ca was applied some intercellular areas remain untransformed even for long time, however when samples were subjected to sa those untransformed areas disappeared and instead finer ausferrite was found. additionally mechanical properties values obtained from tensile and impact tests confirmed that for all times used, sa was superior to the ca.

سوال خود را در مورد این مقاله مطرح نمایید :

با انتخاب دکمه ثبت پرسش، موافقت خود را با قوانین انتشار محتوا در وبسایت تی پی بین اعلام می کنم
مقالات جدیدترین رویدادها
مقالات جدیدترین ژورنال ها